1. Grade:
Pure titanium: TA1, TA2
Titanium alloys: TA10, TC4, TB5
2, specifications:
T 0.5-1.0mm x W1000mm x L 2000-4000mm
T 1.0-5.0mm x W1000-1500mm x L 2000-3500mm
T 5.0- 30mm x W1000-2500mm x L 3000-6000mm
T 30- 80mm x W1000mm x L 2000mm
3. Surface:
Pickled, shiny, sandblasted.
4.Use:
Petrochemical industry, pressure vessels, electroplating equipment and instruments, medical, sporting goods, titanium glasses frames (TB5), titanium watches (TC4 / TA2).
For example, it is rolled and welded into a pressure vessel cylinder (shell) through a rolling plate device, and is drawn through a wire drawing device to produce a titanium mesh plate, which is used to produce a titanium mesh basket commonly used in the electroplating industry.
5. Industry application advantages:
(1) Features and advantages of titanium: light weight, high strength, corrosion resistance, high temperature resistance, bending, stamping, superior mechanical properties, non-toxic and non-magnetic
(2) Advantages of titanium plate electroplating industry:
① Titanium seed plate is an oxide film on the surface, which is equivalent to a good durable abrasion-resistant hair release agent. The use of titanium seed plate saves the release agent, makes the electrode plate easy to peel, and eliminates the pre-treatment process of the seed plate. It is half lighter than a copper seed board.
②The service life of titanium seed board is more than three times that of copper seed board, and it can reach 10 to 20 years according to the operating conditions.
③ The crystal structure of electrolytic copper made from titanium seed plate is dense, the surface is smooth and smooth, and the quality is excellent.
④ Since the titanium seed plate need not be coated with a separating agent, contamination of the copper electrolyte can be avoided.
⑤ Increasing the production capacity and reducing the production cost of electrolytic copper, which has better economic benefits.
Previous: Application Of Titanium And Titanium Alloys In Cardiovascular Repair Materials
prev:Research On Improving Fatigue Life Of Nickel-titanium Alloy
next:Factors, Methods And Processes Affecting The Welding Of Tita