Due to the tendency of titanium alloy material to fill the grinding wheel, it brings difficulties to the grinding of titanium alloy rod and grade 5 titanium alloy. During grinding, the higher temperature rise on the interface between metal and grinding wheel causes higher residual stress on the grinding surface, and the surface finish is not ideal.These difficulties can be basically solved by adopting the following methods:
(1) select a suitable grinding wheel, such as silicon carbide grinding wheel. The sand size is medium (60 ~ 80), the hardness is medium (J ~ m), and the surface speed is 700 ~ 1200m / min. the alumina (aluminum oxide powder or corundum) grinding wheel should be used at a lower speed, such as 550 ~ 600min. Medium grain size is also required.
(2) adopt lower grinding wheel speed and feed speed; Due to the low speed of the grinding wheel, less sparks are generated.
(3) good results can be obtained by cooling with buffer or cutting fluid coolant, ceramic binder and chlorinated or vulcanized cutting oil. No matter what type of coolant is used, it should be well filtered to eliminate the "fishtail" stain caused by titanium particle recycling.
(4) the spark of titanium may catch fire when encountering oil mist, but immersing the workpiece with oil can reduce this danger. Antirust ammonium nitrite aqueous solution can completely eliminate the risk of fire.
but even the best grinding conditions will reduce the fatigue performance of the workpiece.